【摘要】：采用金屬-絕緣體-金屬(MIM)測試結(jié)構(gòu)表征薄膜高頻特性時,差動法能有效地剝離測量過程中寄生效應對表征結(jié)果的消極影響。為此,借助仿真軟件ADS深入探究了差動法中不同內(nèi)徑的結(jié)構(gòu)組合,以及結(jié)構(gòu)中底部電極的厚度和材料對表征結(jié)果的影響。結(jié)果表明:組合DM65-55(兩個結(jié)構(gòu)的內(nèi)徑分別為65μm和55μm)能較大限度剝離寄生效應的影響,其表征精度高達98.7%;底部電極厚度為0.1μm時,能得到較理想的表征結(jié)果;底部電極材料的改變對損耗角正切值的計算影響較大,其均值隨著材料的電阻率減小而減小。
[Abstract]:When the high frequency characteristics of the films are characterized by metal-insulator-metal (MIM), the differential method can effectively peel off the negative effect of parasitic effect on the characterization results. For this reason, the structure combination of different inner diameters in the differential method, and the influence of the thickness of the bottom electrode and the material on the characterization results were investigated by the simulation software ADS. The results show that the combined DM65-55 (65 渭 m and 55 渭 m internal diameters of the two structures) can greatly affect the exfoliation parasitic effect, and the characterization accuracy is up to 98.7m, and the better characterization results can be obtained when the bottom electrode thickness is 0.1 渭 m. The change of the bottom electrode material has a great influence on the calculation of the tangent value of the loss angle, and its mean value decreases with the decrease of the resistivity of the material.
【作者單位】： 桂林電子科技大學機電工程學院;
【基金】：國家自然科學基金資助項目(No.61361004) 廣西科學研究與技術(shù)開發(fā)計劃資助項目(No.桂科轉(zhuǎn)14124005-1-7)
【分類號】：TB383.2

【相似文獻】

相關(guān)期刊論文 前3條

1 向華,曲選輝,郭劍鋒,鄭州順;基于ANSYS的硬質(zhì)合金MIM充模數(shù)值模擬[J];稀有金屬材料與工程;2004年08期

2 楊蘭;郭太良;;場發(fā)射FED器件MIM結(jié)構(gòu)Ta-Ta_2O_5-Al薄膜的制備及性能[J];集美大學學報(自然科學版);2011年06期

3 ;[J];;年期

相關(guān)碩士學位論文 前2條

1 張效敏;[C_（18）mim]～+在蒙脫土層間吸附方式對聚丙烯/蒙脫土復合材料性能的影響[D];合肥工業(yè)大學;2007年

2 何博濤;基于超高速光導開關(guān)的納米級MIM結(jié)構(gòu)串聯(lián)現(xiàn)象的研究[D];天津大學;2007年

，

本文編號：2189850