發(fā)布時(shí)間：2018-07-13 14:31

【摘要】：通過對(duì)比滲透檢測(cè)技術(shù)、X射線數(shù)字成像檢測(cè)技術(shù)和渦流陣列檢測(cè)技術(shù)對(duì)三通-管帽對(duì)接接頭試樣內(nèi)、外表面檢測(cè)的檢測(cè)速度、表面開口應(yīng)力腐蝕開裂檢測(cè)能力和近表面應(yīng)力腐蝕開裂檢測(cè)能力,得出如何有效檢測(cè)在役奧氏體不銹鋼壓力管道應(yīng)力腐蝕開裂的方法。以帶有應(yīng)力腐蝕開裂的三通-管帽試件為檢測(cè)對(duì)象,采用溶劑去除型著色滲透檢測(cè)技術(shù)、X射線數(shù)字成像檢測(cè)技術(shù)和渦流陣列檢測(cè)技術(shù)進(jìn)行試驗(yàn),并對(duì)試驗(yàn)結(jié)果進(jìn)行比較。結(jié)果表明:應(yīng)力腐蝕開裂的面積型缺陷的特有屬性和數(shù)字平板探測(cè)器不能彎曲的特性,會(huì)影響X射線數(shù)字成像檢測(cè)技術(shù)對(duì)管道應(yīng)力腐蝕開裂的檢測(cè)能力,但其對(duì)近表面應(yīng)力腐蝕開裂或埋藏性應(yīng)力腐蝕開裂的檢測(cè)能力仍優(yōu)于渦流陣列檢測(cè)技術(shù)和滲透檢測(cè)技術(shù);渦流陣列檢測(cè)技術(shù)對(duì)表面開口應(yīng)力腐蝕開裂的檢測(cè)能力與滲透檢測(cè)技術(shù)相近,對(duì)近表面應(yīng)力腐蝕開裂的檢測(cè)能力遠(yuǎn)優(yōu)于滲透檢測(cè)技術(shù),檢測(cè)速度也遠(yuǎn)快于滲透檢測(cè)技術(shù),故可在滿足檢測(cè)條件的情況下用渦流陣列檢測(cè)技術(shù)替代滲透檢測(cè)技術(shù)。
[Abstract]:By comparing the penetration detection technology with the X-ray digital imaging technology and the eddy current array testing technology, the detection speed of the inner and outer surfaces of the butt joint of the three-way and tube cap is measured. The detection ability of surface open stress corrosion cracking and near surface stress corrosion cracking is discussed. The effective method for detecting stress corrosion cracking of austenitic stainless steel pressure pipes in service is obtained. Taking the specimen with stress corrosion cracking (SCC) as the test object, the experiment was carried out by using solvent removal coloring penetration detection technique and eddy current array detection technology. The experimental results were compared with each other. The results show that the unique properties of the area type defects of stress corrosion cracking and the non-bending characteristics of digital flat panel detectors will affect the ability of X-ray digital imaging to detect the stress corrosion cracking of pipelines. However, its ability to detect near surface stress corrosion cracking or buried stress corrosion cracking is still superior to eddy current array and penetration detection. The detection ability of eddy current array for surface open stress corrosion cracking is similar to that of osmotic detection, and the detection ability for near surface stress corrosion cracking is much better than that for osmotic detection, and the detection speed is also much faster than that of osmotic detection. Therefore, the eddy current array detection technology can be used to replace the osmotic detection technology under the condition of satisfying the detection conditions.
【作者單位】： 中國(guó)特種設(shè)備檢測(cè)研究院;
【基金】：國(guó)家質(zhì)檢總局科技計(jì)劃資助項(xiàng)目2015QK248(中國(guó)特檢院內(nèi)部科研項(xiàng)目2015內(nèi)03)
【分類號(hào)】：TH49;TG115.28

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 劉洋;;鋁合金應(yīng)力腐蝕開裂的研究進(jìn)展[J];北京聯(lián)合大學(xué)學(xué)報(bào)(自然科學(xué)版);2006年01期

2 孫方遒;;船舶設(shè)備應(yīng)力腐蝕開裂的探討[J];遼寧高職學(xué)報(bào);2007年02期

3 徐勝;艾志斌;;濕硫化氫應(yīng)力腐蝕開裂風(fēng)險(xiǎn)檢驗(yàn)技術(shù)[J];石油化工設(shè)計(jì);2008年03期

4 許世山 ,曹慶國(guó);懸臂彎曲試驗(yàn)方法測(cè)定鈦合金在海水中的應(yīng)力腐蝕開裂敏感性[J];艦船科學(xué)技術(shù);1979年04期

5 黃顯亞;朱祖芳;王得明;肖紀(jì)美;;鈦合金應(yīng)力腐蝕開裂機(jī)理的研究[J];中國(guó)腐蝕與防護(hù)學(xué)報(bào);1982年04期

6 James L.Gossett,袁競(jìng)雄;應(yīng)力腐蝕開裂的防止[J];化工裝備技術(shù);1983年S1期

7 高娃,侯振聲;鈦合金的應(yīng)力腐蝕開裂分析[J];鈦工業(yè)進(jìn)展;1997年05期

8 蔡志安;李春福;;20鋼在不同介質(zhì)中的硫化物應(yīng)力腐蝕開裂敏感性[J];機(jī)械工程材料;2014年01期

9 K.Krist L.Leewis,M.Wilmoff,廖柯熹,方芳,姚安林;天然氣管線應(yīng)力腐蝕開裂機(jī)理[J];國(guó)外油田工程;2000年12期

10 曾為民,敖建平,金石;干涉配合構(gòu)件的應(yīng)力腐蝕開裂特性[J];南昌航空工業(yè)學(xué)院學(xué)報(bào);2000年01期

相關(guān)會(huì)議論文 前10條

1 賈維平;朱自勇;柯偉;韓恩厚;鄭宇禮;;銅雙晶體的應(yīng)力腐蝕開裂行為[A];疲勞與斷裂2000——第十屆全國(guó)疲勞與斷裂學(xué)術(shù)會(huì)議論文集[C];2000年

2 盧志明;高增梁;;16MnR鋼在液氨環(huán)境中的應(yīng)力腐蝕開裂試驗(yàn)研究[A];2004年全國(guó)化工、石化裝備國(guó)產(chǎn)化暨設(shè)備管理技術(shù)交流會(huì)會(huì)議論文集[C];2004年

3 呂戰(zhàn)鵬;莊子哲雄;陳俊R，

本文編號(hào)：2119702