  本文選題：高溫形狀記憶 + Ni-Mn-Ga合金　； 參考：《稀有金屬材料與工程》2017年09期

【摘要】：通過(guò)彎曲試驗(yàn)研究了雙相Ni_(58)Mn_(25)Ga_(16.9)Gd_(0.1)合金的形狀記憶效應(yīng)和回復(fù)率。結(jié)果表明,該合金具有優(yōu)異的形狀回復(fù)能力。在預(yù)變形4.6%加熱后,可以得到86%的形狀回復(fù)率,高于已報(bào)道的雙相Ni-Mn-Ga合金。這是因?yàn)镚d摻雜提高了γ相的臨界滑移應(yīng)力,使γ相不易發(fā)生變形。
[Abstract]:The shape memory effect and the recovery rate of the biphasic NiStack58 Mn-MN _ (25) GdSZ _ (0.1) alloy have been studied by means of bending test. The results are as follows: (1) the shape memory effect and the recovery rate of the alloy are studied. The results show that the alloy has excellent shape recovery ability. After predeformation of 4.6% heating, 86% shape recovery can be obtained, which is higher than the reported dual phase Ni-Mn-Ga alloy. This is because Gd doping increases the critical slip stress of 緯 phase and makes 緯 phase difficult to deform.